thermocouple wire

K J  E T N type Thermocouple Wire  

Fe-CuNi(Constantan)  (Type J)  thermocouple wire

Fe-CuNi (type J)  thermocouple wire is also named Fe- Constantan thermocouple wire . The positive leg Fe(JP) is made by pure Iron, and the main chemical composition of negative leg Constantan (JN) is Cu: Ni≈ 55%: 45%. Although they are all called Constantan, JN does not give the same EMF output curve as EN and TN, it cannot be instead by other Constantan.

The operating temperature range of type J thermocouple wire  is -210~1200°C, but it is usually used in the temperature range 0~750°C due to embrittlement of Iron.

Type J thermocouple wire  has good resistance to oxidation and high EMF output against Platinum 67, with good temperature accuracy, sensitivity and stability. It is recommended for vacuum, oxidizing, reducing or inert atmospheres, but it can not be used in sulphurous atmosphere above 500°C. 

NiCr-CuNi(Constantan) (Type E)  thermocouple wire

NiCr- CuNi (type E)  thermocouple wire is also named NiCr- Constantan thermocouple wire . The main chemical composition of positive leg NiCr (EP) is Ni: Cr≈90:10; negative leg Constantan (EN) is Cu: Ni≈ 55%: 45%. Although EN, TN, JN are all called Constantan, EN and TN don not give the same EMF output curve as JN. EN and TN are able to interchange but they are not interchangeable with JN. The operating temperature range of type E thermocouple is -200~900°C.

Type E thermocouple wire  has the largest EMF output and highest sensitivity, so it is ideal for measuring small temperature change. It also has good stability in the low temperature range up to 300°C, and good property of anti-corrosion in humidity atmosphere. It is recommended for oxidizing or inert atmospheres, but cannot be used directly in reducing atmosphere and atmosphere with sulphur gases.

Nicrsi-NisiMg (Type N)  thermocouple wire

Nicrsi-NisiMg (Type N) thermocouple wire is the latest base metal thermocouple, developed to improve the drawbacks that type K thermocouple wire has. The main chemical composition of positive leg Nicrsi (NP) is Ni: Cr: Si≈84.4: 14.2: 1.4; negative leg NisiMg (NN) is Ni: Si: Mg≈95.5: 4.4: 0.1. Type N thermocouple also be used in the similar atmospheres that type K works, and the operating temperature range is -200~1300°C.

Type N thermocouple wire  improves the EMF drift and short term EMF change, compared to type K thermocouple wire, and has a longer life than type K thermocouple wire. Therefore, in the industries where temperature control and measurement are especially critical, type N thermocouple wire has more advantages than other thermocouple wire as it has long life and stable thermal EMF.

Cu-CuNi (Constantan) (Type T)  thermocouple wire

Cu-CuNi (type T) thermocouple wire is also named Cu- Constantan thermocouple wire. The positive leg Cu(TP) is made by pure Copper, and the main chemical composition of negative leg Constantan (TN) is Cu: Ni≈ 55%: 45%. Although EN, TN, JN are all called Constantan, TN and EN don not give the same EMF output curve as JN. EN and TN are able to interchange but they are not interchangeable with JN. The operating temperature range of type T thermocouple wire is -200~350°C, Due to the low resistance of oxidation that Copper has, it is not advisable to go beyond that range.

Type T thermocouple wire  has good resistance to oxidation, high EMF output, with good temperature accuracy, sensitivity and stability. In the temperature range -200~0°C, it has better property, the year stability is less than ±3μV 