Brand Name: HAIXU
Model Number: 0-1mm,1-3mm,3-5mm,5-8mm,200#-0,320#-0
Place of Origin: China
Description:
Tabular Alumina is high-density, fully shrunk, coarse crystalline alpha alumina that have been converted to the corundum form. It is a completely recrystallized a-al2o3 sintered at slightly below the melting point of imported alumina after batching, grinding and molding.
Tabular Alumina is produced by sintering ball-formed calcined alumina at a temperature under the 2040°C fusion point of aluminum oxide. The crystals are arranged in a tabular staggered way, which increases the mechanical strength of the particles.
Properties:
1. High purity up to 99.5% Al2O3
2. Good resistance to alkalis and mineral acids
3. Low water absorption less than 1%
4. High hardness and toughness
5. High thermal conductivity
6. Excellent thermal shock resistance
7. Good abrasion resistance.
8. High volume stability
9. High anti-bending strength
Applications:
Tabular Alumina is widely used in refractories including sliding gate, purging plug brick, nozzle, well block as well as kiln furniture, electronic industries, petrochemical industries and ceramic industries. The usage of tabular alumina almost covers every step in steeling manufacturing.
Technical data:
Typical physical properties |
||||
Specific gravity |
3.96 g/cm3 |
|||
Bulk density |
3.55 g/cm3 |
|||
Volume denstiy |
3.45-3.5g/cm3 |
|||
Apparent porosity |
4-6% |
|||
water absorption |
1-1.5% |
|||
Mohs' Hardness |
9 |
|||
Knoop hardness |
2000kg/cm3 |
|||
Thermal conductivity |
(100℃)0.069 cal/sec cm℃ |
|||
Heat capacity |
(20℃)0.21cal/gm/(100℃) |
|||
Melting temperature |
2040℃ |
|||
Refractive Index |
1.76 |
|||
Apperance |
White crystalline granules or powder |
|||
Chemical composition(%) |
||||
Size |
AL2O3 |
SiO2 |
Fe2O3 |
Na2O |
0-1mm 1-3mm 3-5mm 5-8mm |
min 99.2 |
max 0.1 |
max 0.02 |
max 0.4 |
200#-0 320#-0 325# |
min 99.1 |
max 0.15 |
max 0.04 |
max 0.4 |
Customized size is available upon request |